Mirakutoran®TPU E395
热塑性聚氨酯弹性体合金
Japan Mirakutoran Inc.
产品说明:
Our TPU "Mirakutoran ®" has the following outstandingfeatures.
Has excellent wear resistance
Tensile strength, high mechanical strength and tear strength
Is a wide range of hardness
High impact strength
Oil resistance and good chemical resistance
Excellent low temperature properties, weather resistance, ozoneresistance and is also good
Flexible rubber elastic, vibration-effective silencing
Compared to other urethane elastomer thermoplastic that ismore
Playback can be processed
Vulcanization process without curing reaction, very highproductivity
Resins and other polymer is easy
Solution is easily dissolved in solvent process
Mirakutoran to the standard type E and P are two types.
Type E has a certain cross-linked structure in the molecule, andexcellent mechanical strength and compression set. P type ischaracterized by good liquidity linear structure
Mirakutoran® TPU E395 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.12 | g/cm3 | ASTM D792 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | ASTM D2240 | ||
| 邵氏A, 23°C, 2.00 mm, 注塑 | 93 到 97 | ASTM D2240 | |
| 邵氏D, 23°C, 2.00 mm, 注塑 | 46 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 泰伯耐磨性 (23°C,1000 Cycles, 1000 g, H-22 转轮) | 45.0 | mg | ASTM D1044 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 1(应变,23°C, 2.00 mm) | 12.0 | MPa | ASTM D412 |
| 抗张强度 2(屈服,23°C, 2.00 mm) | 48.0 | MPa | ASTM D412 |
| 伸长率 3(断裂,23°C, 2.00 mm) | 480 | % | ASTM D412 |
| 撕裂强度 4(23°C,2.00 mm) | 137 | kN/m | ASTM D624 |
| Rebound Resilience (23°C,2.00 mm) | 45 | % |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 120 | °C | ASTM D1525 5 |
| 补充信息 |
|---|
| Test Methods: JIS K7311, K6262, K7206 |
| 备注 | |
|---|---|
| 1 . | 300 mm/min |
| 2 . | 300 mm/min |
| 3 . | 300 mm/min |
| 4 . | 300 mm/min |
| 5 . | 压 力1 (10N |